Specific heat of the iron-based high- Tc superconductor SmO1-xFxFeAs
Abstract
The specific heat C(T) of iron-based high- Tc superconductor SmO1-xFxFeAs (0≤x≤0.2) was systematically studied. For the undoped x=0 sample, a specific heat jump was observed at 130K . This is attributed to the structural or spin-density-wave transition, which also manifests on resistivity as a rapid drop. However, this jump disappears with slight F doping in the x=0.05 sample, although the resistivity drop still exists. The specific heat C/T shows clear anomaly near Tc for x=0.15 and 0.20 superconducting samples. Such anomaly has been absent in LaO1-xFxFeAs . For the parent compound SmOFeAs , C(T) shows a sharp peak at 4.6K , and with electron doping in the x=0.15 sample, this peak shifts to 3.7K . It is interpreted that such a sharp peak results from the antiferromagnetic ordering of Sm3+ ions in this system, which mimics the electron-doped high- Tc cuprate Sm2-xCexCuO4-δ .
- Publication:
-
Physical Review B
- Pub Date:
- May 2008
- DOI:
- 10.1103/PhysRevB.77.180510
- arXiv:
- arXiv:0804.3642
- Bibcode:
- 2008PhRvB..77r0510D
- Keywords:
-
- 74.25.Bt;
- 74.25.Ha;
- Thermodynamic properties;
- Magnetic properties;
- Condensed Matter - Superconductivity;
- Condensed Matter - Strongly Correlated Electrons
- E-Print:
- 4 pages, 4 figures