Spin-Transfer Switching and Thermal Stability in an FePt/Au/FePt Nanopillar Prepared by Alternate Monatomic Layer Deposition
Abstract
We fabricated a current-perpendicular-to-plane giant magnetoresistance (CPP-GMR) nanopillar with a 1-nm-thick FePt free layer having perpendicular anisotropy using the alternate monatomic layer deposition method. Nanopillars consisting of [Fe (1 monolayer (ML))/Pt (1 ML)]n (n: the number of the alternation period) ferromagnetic layers and an Au spacer layer showed spin-transfer induced switching at room temperature. An average critical switching current density (Jc0) of 1.1×107 A/cm2 with a large thermal stability parameter (Δ) of 60 was obtained in a nanopillar with a free-layer thickness of 1.02 nm (n=3) and a pillar diameter of 110 nm. The ultrathin free-layer with high perpendicular anisotropy is effective to obtain both large Δ and small Jc.
- Publication:
-
Applied Physics Express
- Pub Date:
- April 2008
- DOI:
- 10.1143/APEX.1.041302
- arXiv:
- arXiv:0804.0688
- Bibcode:
- 2008APExp...1d1302Y
- Keywords:
-
- Condensed Matter - Materials Science
- E-Print:
- 11 pages