Magnetic field induced ferroelectric loop in Bi0.75Sr0.25FeO3-δ

Magnetic field induced ferroelectric hysteresis loop observed in Bi_0.75Sr_0.25FeO_3-δ is of prime importance. The coexistence of antiferromagnetism and weak ferromagnetism is responsible for the original magnetoelastic and magnetoferroelectric properties. Upon external magnetic field application, the existence of a magnetostrictive effect supports a structural transition toward a homogeneous antiferromagnetic and ferroelectric phase. The magnetic field induced polarization is among the highest reported for Bi_{FeO3 based systems in either thin film or bulk form (Pr}=96μC /cm² at 10T) while the ferroelectric coercive field is among the lowest reported (H_c=661V/cm at 10T). These properties make this material very attractive for technical applications.