High Strain and Strain-Rate Behaviour of PTFE/Aluminium/Tungsten Mixtures
Abstract
Conventional drop-weight techniques were modified to accommodate low-amplitude force transducer signals from low-strength, cold isostatically pressed 'heavy' composites of polytetrafluoroethylene, aluminum and tungsten. The failure strength, strain and the post-critical behavior of failed samples were measured for samples of different porosity and tungsten grain size. Unusual phenomenon of significantly higher strength (55 MPa) of porous composites (density 5.9 g/cc) with small W particles (less than 1 micron) in comparison with strength (32 MPa) of dense composites (7.1 g/cc) with larger W particles (44 microns) at the same volume content of components was observed. This is attributed to force chains created by a network of small W particles. Interrupted tests at different levels of strain revealed the mechanisms of fracture under dynamic compression.
- Publication:
-
arXiv e-prints
- Pub Date:
- November 2007
- DOI:
- 10.48550/arXiv.0711.1191
- arXiv:
- arXiv:0711.1191
- Bibcode:
- 2007arXiv0711.1191A
- Keywords:
-
- Condensed Matter - Soft Condensed Matter;
- Condensed Matter - Materials Science
- E-Print:
- 4 pages, 6 figures, paper is in press in Proceedings of the Conference of the American Physical Society Topical Group on Shock Compression of Condensed Matter, American Institute of Physics,2008