The Ba2LnFeNb4O15 Tetragonal Tungsten Bronze: towards RT composite multiferroics
Abstract
Several Niobium oxides of formula Ba2LnFeNb4O15 (Ln = La, Pr, Nd, Sm, Eu, Gd) with the Tetragonal Tungsten Bronze (TTB) structure have been synthesised by conventional solid-state methods. The Neodymium, Samarium and Europium compounds are ferroelectric with Curie temperature ranging from 320 to 440K. The Praseodymium and Gadolinium compounds behave as relaxors below 170 and 300 K respectively. The Praseodymium, Neodymium, Samarium, Europium and Gadolinium compounds exhibit magnetic hysteresis loops at room temperature originating from traces of a barium ferrite secondary phase. The presence of both ferroelectric and magnetic hysteresis loops at room temperature allows considering these materials as composites multiferroic. Based on crystal-chemical analysis we propose some relationships between the introduction of Ln3+ ions in the TTB framework and the chemical, structural and physical properties of these materials.
- Publication:
-
arXiv e-prints
- Pub Date:
- July 2007
- DOI:
- 10.48550/arXiv.0707.3112
- arXiv:
- arXiv:0707.3112
- Bibcode:
- 2007arXiv0707.3112J
- Keywords:
-
- Condensed Matter - Materials Science
- E-Print:
- Revised version after identification of a spurious barium ferrite phase responsible for composite multiferroic properties at RT. Appearance of this parasitic phase is correlated to the crystal-chemistry of the Ba2LnFeNb4O15 TTBs. Submitted to Solid State Sciences. 27 pages, 7 figures, 3 tables