Microstructure Characteristics of ECAP Processed 1050 Aluminum After Deformation and 5 Years Later
Abstract
Modification of microstructure parameters of severely deformed 1050 aluminum after 5 years of recovery at ambient temperature was studied. The samples of 1050 aluminum were extruded using ECAP technique. The EBSD maps were recorded for the initial material and for the deformed samples. Next, the latter samples were left at ambient temperature during 5 years and a full EBSD study of the material was repeated. It was found that all microstructure parameters and textures have changed after this period. This is due to recovery and partial recrystallization, which took place in the samples during 5 years. The presented modifications of material microstructure are important, e.g., in the aspect of long time service of mechanical parts produced by severe plastic deformation techniques.
- Publication:
-
Metals and Materials International
- Pub Date:
- August 2021
- DOI:
- 10.1007/s12540-020-00817-3
- Bibcode:
- 2021MMI....27.2720W
- Keywords:
-
- Severe plastic deformation;
- Equal channel angular pressing;
- Electron backscatter diffraction;
- Microstructure parameters;
- Texture;
- Recovery