The Effects of Al2O3 and SiO2 on the Formation Process of Silico-Ferrite of Calcium and Aluminum (SFCA) by Solid-State Reactions
Abstract
The silico-ferrite of calcium and aluminum (SFCA) is a significant crystalline phase that bonds in high basicity sinter. Al2O3 and SiO2 play an important role in the formation of SFCA in the Fe2O3–CaO–SiO2–Al2O3 system, but the effect mechanism of Al2O3 and SiO2 on the formation of SFCA is unclear. To investigate this effect, sintering experiments were carried out with different temperatures and different times. It was found that the reaction of Al2O3 with CaFe2O4 (CF) as an initial product was easier to form during the calcium iron aluminum oxide (CFA) than that of SiO2 with CF to form SFC. This was due to the former directly forming to CFA while the latter initially formed Ca2SiO4 (C2S) and Ca2.5Fe15.5O25, and then SFC. It was also observed that when Al2O3 and SiO2 existed simultaneously, the Al2O3 initially reacted with CF to form CFA at 1100 °C, while the SiO2 participated in the formation of SFCA at 1150 °C without the formation of SFC. Moreover, it was understood that these were different effects in that the Al2O3 promoted the transformation from the orthorhombic crystal system to the triclinic crystal system, while the SiO2 dissolved into CFA to form the SFCA phase when Al2O3 existed.
- Publication:
-
Minerals
- Pub Date:
- February 2019
- DOI:
- 10.3390/min9020101
- Bibcode:
- 2019Mine....9..101L
- Keywords:
-
- Al2O3;
- SiO2;
- SFCA;
- formation process;
- solid-state reactions