Strength and deformation mechanisms of rhyolitic glass at lower seismogenic zone conditions

Although its relevance to coseismic earthquake source properties is still debated, frictional melting and the production of quenched glass called pseudotachylyte is a recurring process in some earthquake source regions. To investigate how glassy materials affect the post- and interseismic- strength and stability of faults, rhyolitic obsidian gouges were sheared under dry and wet conditions from 200 °C to 300 °C at effective normal stresses up to 200 MPa. Velocity-stepping and slide-hold slide tests were performed for up to three days. Dry glass gouges exhibited a brittle rheology at all conditions tested, exhibiting friction values and microstructures consistent with siliciclastic materials. Likewise, wet glass gouges at 200 °C exhibited a brittle rheology. In contrast, wet gouges at 300 °C transitioned from brittle sliding to linear-viscous (Newtonian) flow at strain rates < 3x10-4 s-1, indicating melt-like behavior well below the equilibrium melting temperature. The melt ranged from 2.1x1011 to 2.6x1012 Pa-s. The molten gouges transitioned back to glass when strain rates were increased, which, in some cases, promoted extreme strengthening. The molten gouges were fully welded with rod-shaped microlites rotated and boudinaged into the flow direction. There was very little evidence for nucleation of new phases within the glass or metasomatic alteration. Fourier transform infrared spectroscopy along with electron backscatter imaging demonstrate that hydration of the glass by diffusion of pore water was the dominant process reducing the viscosity and promoting melt flow. As much as 5 wt% water diffused into the nominally anhydrous glass. These results may provide insight into postseismic-slip behaviors and challenge some interpretations of fault kinematics which assume pseudotachylyte formation and flow is solely coseismic.