Hydrogenation thermodynamics of melt-spun magnesium rich Mg-Ni nanocrystalline alloys with the addition of multiwalled carbon nanotubes and TiF3
Abstract
Based on the complexity of hydrogen absorption/desorption process and from the perspective of overall control, the as-cast Mg-10wt%Ni (Mg10Ni) alloy has been successively optimized by melt-spinning and surface catalyzed to realize the internal refinement as well as surface modification. The isothermal hydrogenation behavior of modified Mg-rich alloys has been investigated in this work. The results indicate that melt-spun Mg10Ni catalyzed by multiwalled carbon nanotubes (MWCNTs) coupling with TiF3 possesses superior activation properties and can absorb 6.23 wt% at 250 °C under 2.5 MPa. It is worth mentioning that the hydrogenation capacities of Mg10Ni-MWCNTs-TiF3 are 5.93 wt% and 5.99 wt% within the initial 1 min and 5 min, respectively. Meanwhile, the catalytic effect of MWCNTs and TiF3 has been discussed. The improved activation performance as well as the thermodynamics properties of Mg10Ni catalyzed by MWCNTs and TiF3 is attributed to the synergistic effect on dissociation of H2 molecules, diffusion of H-atoms and heterogeneous nucleation of hydrides.
- Publication:
-
Journal of Power Sources
- Pub Date:
- February 2016
- DOI:
- 10.1016/j.jpowsour.2015.12.050
- Bibcode:
- 2016JPS...306..437H
- Keywords:
-
- Magnesium rich alloys;
- Rapid solidification;
- Activation;
- Kinetics;
- Thermodynamics;
- Synergetic catalytic