Tensile properties of precracked tempered martensitic steel specimens tested at ultralow strain rates in high-pressure hydrogen atmosphere
Abstract
Tensile tests were performed on precracked Cr-Mo martensitic steel (C: 0.38, Si: 0.22, Mn: 0.84, P: 0.024, S: 0.021, Ni: 0.08, Cr: 1.11, Mo: 0.15, Cu: 0.12, Fe: bal. (wt%)) specimens at various strain rates (ranging from 6.5 × 10-8 s-1 to 1.0 × 10-4 s-1) in high-pressure (95 MPa) hydrogen and helium atmospheres. Irrespective of the strain rate, the tensile strength in the helium atmosphere was 1400 MPa. In the hydrogen atmosphere, the tensile strength decreased to less than 600 MPa at a strain rate of 2.0 × 10-5 s-1. However, the tensile strength increased to 900 MPa when the strain rate was decreased to 6.5 × 10-8 s-1. This recovery of the tensile strength was because of the decrease in the local stress in the vicinity of the precrack because of hydrogen.
- Publication:
-
Philosophical Magazine Letters
- Pub Date:
- May 2015
- DOI:
- 10.1080/09500839.2015.1049574
- Bibcode:
- 2015PMagL..95..260S
- Keywords:
-
- hydrogen in metal;
- low strain rate;
- precracked specimen;
- hydrogen-enhanced localized plasticity;
- hydrogen-enhanced decohesion