The modem study a thermal martensitic transformation of biomedical Co-Cr-Mo alloys and ultimately offers large elongation to failure while maintaining high strength. In the future study, structural evolution and dislocation slip as an elementary process in the martensitic transformation in Co-Cr-Mo alloys were investigated to reveal the origin of their enhanced phase stability due to nitrogen addition and coating of calcium phosphate specimens with and without nitrogen addition were prepared. The N-doped alloys had a single-phase matrix, whereas the N-free alloys had a duplex microstructure. Irrespective of the nitrogen content, dislocations frequently dissociated into Shockley partial dislocations with stacking faults. The Nano range coating of calcium phosphate function as obstacles to the glide of partial dislocations and consequently significantly affect the kinetics of the martensitic transformation. As a result, the formation of marten site plays a crucial role in plastic deformation and wear behavior, the developed nanostructures modification associated with nitrogen addition must be a promising strategy for highly durable orthopedic implants.