Dielectric spectroscopy of Dy2O3 doped (K0.5Na0.5)NbO3 piezoelectric ceramics

We report the dielectric properties of ( K 0.5 Na 0.5 ) NbO 3 ceramics doped with x wt% of Dy 2 O 3 (x= 0.0-1.5 wt%) using the broadband dielectric spectroscopy. The X-ray diffraction studies showed the formation of perovskite structure signifying that Dy 2 O 3 diffuse into the KNN lattice. Samples doped with x > 0.5 wt% exhibit smaller grain size and lower relative densities. The dielectric properties of KNN ceramics doped with Dy 2 O 3 are enhanced by increasing the ^{Dy 3+} content; among the compositions studied, x = 0.5 wt% exhibited the highest dielectric constant and lowest loss at 1MHz over the temperature range of 30°C to 400°C. All the samples exhibit maximum dielectric constant at the Curie temperature (∼ 326°C) and a small peak in the dielectric constant at around 165°C is due to a structural phase transition.

At the request of all authors, and by agreement with the Proceedings Editors, a corrected version of this article was published on 19 June 2014. The full text of the Corrigendum is attached to the corrected article PDF file.