According to the reformed Cassie-Baxter equation, the superhydrophobic phenylenebenzobisoxazole (PBO) fiber bundle boats were fabricated from mimicking the lotus leaf venation using chemical surface modifications and roughness introduction. Water contact angles as high as 152.3° were achieved for PBO fiber bundles. Furthermore, the loading capacities of the superhydrophobic PBO fiber bundle boats were also measured. And the highest loading weight, 8.36 g, was obtained by the boats treated with 2.0 wt.% (heptadecafluoro-1,1,2,2,-tetradecyl)trimethoxysilane (HFTES). The large loading capacities were believed to arise from the air film surrounding the superhydrophobic surfaces of boats. The results of this study presented new applications of artificial hydrophobic surfaces in areas of miniature aquatic devices.