IR-induced nonlinear optics in Ge-doped Bi 12TiO 20 large-sized nanocrystallites

Photoinduced non-linear optical effects in large-sized (up to 25 nm) nanocrystallites (NC) of Ge-doped Bi ₁₂TiO ₂₀ (BTO:Ge) incorporated within olygoether photopolymer matrix have been studied. Photoinduced second harmonic generation (PISHG) was measured. Nd:YAG pulsed laser (λ=1.06 μm) was used as a source of photoinducing light. As a fundamental light source for the SHG and two-photon absorption, Er:LiYF ₄ laser (λ=2.065 μm) was used. We have found that with increasing IR pump power density, the output doubled frequency SHG signal (λ=1.03 μm) increases and achieves its maximum value at the pump power density about 0.45 GW/cm ² and NC size about 12 nm.The values of second-order optical susceptibilities were almost 20% larger than for the pure BTO NC single crystals. With decreasing temperature below 60 K, the SHG signal increases achieving maximal value at LHeT.