Processing, microstructure, and properties of β titanium alloys modified with boron
Abstract
The development of next-generation βTi alloys is expected to involve very attractive combinations of strength-toughness-fatigue resistance at large cross sections, improved and affordable thermomechanical processing, and enhanced elevated temperature capability. This article describes the development of βTi alloys that are modified with small boron (B) additions to achieve these goals. Two important aerospace alloys, Ti-15Mo-2.6Nb-3Al-0.2Si and Ti-5Al-5V-5Mo-3Cr microalloyed (0.1%) with B were considered. Ingots that were 70 mm in diameter and 500 mm in length were cast using induction skull melting. A detailed microstructural characterization and tensile property evaluation were conducted. Microalloying with B refines the cast grain size to about 50 µm, which enhances strength and ductility. The effect of B additions on the microstructural stability and properties in the as-cast condition was established. The implications of B additions on the microstructural evolution and affordability of subsequent processing is also discussed.
- Publication:
-
Journal of Materials Engineering and Performance
- Pub Date:
- December 2005
- DOI:
- 10.1361/105994905X75547
- Bibcode:
- 2005JMEP...14..741T
- Keywords:
-
- β
- titanium alloys;
- B addition;
- cast alloys;
- microstructure;
- properties;
- β titanium alloys