Effective gain measurements in chromium-doped forsterite

Effective gain cross section in tetravalent chromium-doped forsterite laser crystal was measured over the 1180-1330 nm spectral range. The experiment was performed using two collinear laser beams in a pump-and-probe arrangement. The peak-gain cross section from this measurement is estimated to be 1.9 x 10 to the -19th sq cm at 1215 nm, which is comparable to the value of about 2 x 10 to the -19th sq cm predicted by fluorescence linewidth and lifetime measurements. These results indicate that excited-state absorption is not a major loss mechanism in tetravalent chromium-doped forsterite.