The Selective Epitaxy of Silicon at Low Temperatures.

This dissertation has developed a process for the selective epitaxial growth (SEG) of silicon at low temperatures using a dichlorosilane-hydrogen mixture in a hot-wall low pressure chemical vapor deposition (LPCVD) reactor. Some basic issues concerning the quality of epilayers --substrate preparation, ex-situ and in-situ cleaning, and deposition cycle, have been studied. We find it necessary to use a plasma etch to open epitaxial windows for the SEG of Si. A cycled plasma etch, a thin sacrificial oxide growth, and an oxide etching step can completely remove plasma-etch-induced surface damage and contaminants, which result in high quality epilayers. A practical wafer cleaning step is developed for low temperature Si epitaxial growth. An ex-situ HF vapor treatment can completely remove chemical oxide from the silicon surface and retard the reoxidation of the silicon surface. An in-situ low-concentration DCS cycle can aid in decomposition of surface oxide during a 900 ^circC H_2 prebake step. An HF vapor treatment combined with a low-concentration of DCS cycle consistently achieves defect-free epilayers at 850^circC and lower temperatures. We also show that a BF_sp{2}{+ } or F^+ ion implantation is a potential ex-situ wafer cleaning process for SEG of Si at low temperatures. The mechanism for the formation of surface features on Si epilayers is also discussed. Based on O ^+ ion implantation, we showed that the oxygen incorporation in silicon epilayers suppresses the Si growth rate. Therefore, we attribute the formation of surface features to the local reduction of the Si growth rate due to the dissolution of oxide islands at the epi/substrate interface. Finally, with this developed process for the SEG of silicon, defect-free overgrown epilayers are also obtained. This achievement demonstrates the feasibility for the future silicon-on-oxide (SOI) manufacturing technology.