Corrosion in NiCd cells
Abstract
Corrosion in the terminals of nickel cadmium cells was investigated. Corrosion, crevice type corrosion, at the interface between the stainless steel material, the nickel material, and the braze was examined. It was concluded that in the welded areas there was no problem. There was corrosion of the crevice type in the brazed areas and some pitting was evident between the braze and the base material.
- Publication:
-
The 1980 Goddard Space Flight Center Battery Workshop
- Pub Date:
- March 1981
- Bibcode:
- 1981batt.work..415B
- Keywords:
-
- Electrochemical Corrosion;
- Electrodes;
- Life (Durability);
- Nickel Cadmium Batteries;
- Pitting;
- Brazing;
- Cracks;
- Defects;
- Degradation;
- Electrochemical Cells;
- Interfaces;
- Service Life;
- Stainless Steels;
- Welded Structures;
- Electronics and Electrical Engineering