Effect of the morphology of adsorbed oleate on the wettability of a collophane surface
Abstract
The adsorption of surfactants on a solid surface could alter its wettability, which offers a wide range of relevant applications such as mineral flotation, hydrophobic material preparation and nanomaterial dispersion. The morphology of adsorbed oleate on a collophane surface was visualized using the peakforce tapping mode of atomic force microscopy (AFM), and its effect on the wettability of collophane was analysed by contact angle measurements, adsorption measurements and molecular dynamics (MD) simulations. The AFM images demonstrated that the adsorbed structure varied with different oleate concentrations. First, the small cylindrical micelles with concomitant monolayer and bilayer structures were observed above the hemimicelle concentration (hmc) of 1 × 10-5 mol/L, which enhanced the hydrophobicity of the collophane surface, and the collophane surface was not completely covered with the oleate monolayer due to surface heterogeneity. Then, large cylindrical micelles with a major bilayer were formed as the critical micelle concentration (cmc) of 1 × 10-3 mol/L was approached, which decreased its hydrophobicity, and finally the formation of large cylindrical micelles with multilayer at the cmc caused the hydrophilicity of the collophane surface. Therefore, there was a suitable equilibrium concentration between the hmc and cmc for oleate as a collector during mineral flotation, and oleate could also be used as a dispersant for colloidal stability when its equilibrium concentration reached the cmc. The effect of the adsorbed structure on the wettability of collophane was also confirmed by MD simulations. This study provides a good understanding of the surface modification of particles by surfactants for flotation and dispersion applications.
- Publication:
-
Applied Surface Science
- Pub Date:
- June 2018
- DOI:
- 10.1016/j.apsusc.2018.03.020
- Bibcode:
- 2018ApSS..444...87Y
- Keywords:
-
- Collophane;
- Sodium oleate;
- Adsorption;
- Wettability;
- Atomic force microscopy;
- Molecular dynamics simulation