Residual stress determination in thick welded steel plates

Through thickness strain distribution of 50 mm thick welded ferritic steel (bcc) plate was studied using diffraction reflections 211 and 110 and neutron wavelengths of 1.55 and 2.39Å, respectively. Experimental results showed that for stress measurements in a possibly maximum thick weld, the different strain components should be measured with different reflections 211 and 110. The strains measured with these reflections for the same component are close. Since planes (211) and (110) of bcc ferrite have the same diffraction elastic constants the appropriate values of stresses could be derived from strains measured with reflections 211 and 110.